Nickel 200 / 201 Pipe & Tubing

Nickel 200 is 99 .6% pure nickel, among the most difficult metals. The Nickel 200’s features consist of superior mechanical properties, minimal gas content, lower vapor- stress, magnetic elements, and also higher thermal and electrical conductivity. The properties and its chemical components make Nickel 200 fabricatable and also seriously resistant against corrosive environment. Nickel 200 is helpful in almost any environment below 600º F. It will be greatly resistant against corrosion by neutral and also alkaline salt solutions. The rust resistance of Nickel 200 will make it mainly helpful for sustaining product purity in the managing of foods, synthetic fibers, and caustic alkalies; Nickel 200 has reduced corrosion rates in neutral or distilled water. The metallic may be hot produced to any specific shape and also formed cold by almost all methods. Additionally, in structural applications exactly where resistance to rust is an excellent consideration. Additional applications consist of chemical shipping drums, electrical and also electronic components, and aerospace and also missile parts.

Nickel 201 are solid solution improved, commercially 100% pure wrought components. Usually, the elemental restrictions of each alloys are joined into one, dual-certified chemistry leading to one alloy with the preferred features of both alloys.Nickel 201 may be hot formed to nearly every shape. The heat range 1200°F to 2250°F recommended and has to be cautiously abided as the appropriate temperature is an essential element in reaching hot malleability. Complete information of the forming procedure needs to be sought or understood before proceeding.Nickel 201 could be cold formed by all of the conventional techniques , but since nickel alloys have better stiffness compared to stainless steels more energy is needed to carry out the operations . Nickel 201 is the lower carbon form of Nickel 200. It can be preferred to Nickel 200 for applications including exposure to temperature ranges above 600°F. With lower base hardness and also decrease work-hardening rate, this is especially designed for cold forming.

Standards – Nickel 200 / 201 Pipe & Tubing

Summary Standards
Standard Specification for Nickel Seamless Pipe and Tube ASTM B 161
Standard Specification for Seamless Nickel and Nickel Alloy Condenser and Heat-Exchanger Tubes ASTM B 163
Standard Specification for Welded Nickel (UNS N02200/UNS N02201) and Nickel Copper Alloy (UNS N04400) Pipe ASTM B 725
Standard Specification for Welded Nickel (UNS N02200/UNS N02201) and Nickel Copper Alloy (UNS N04400) Tube ASTM B 730

Mechanical Properties – Nickel 200 / 201 Pipe & Tubing

Tensile Strength : Unit – ksi (MPa) , Minimum
Yeild Strength : 0.2 % Offset , Unit – ksi (MPa) , Minimum
Elongation : in 2″, Unit : % , MinimumValues as per ASTM B 163

Condition & Grade Tensile Strength Yeild Strength Elognation
Annealed Nickel 200 55 (379) 15 (103) 40
Annealed Nickel 201 50 (345) 12 (83) 40

Heat Exchanger

Welded Pipe

Nickel 200 / 201 Pipe

Stocking & Supplying Seamless & Welded Pipes as small as 1/4″ NB and 6″ NB. Thickness ranging from Sch 10 to Sch 80.

Tube / Tubing

Nickel 200 / 201 Tube / Tubing

Stocking & Supplying Seamless & Welded Tubes / Tubing from 6mm OD to 101.6mm OD. Thickness ranging from 0.8mm to 6mm.